G115钢<inline-formula><alternatives><math xmlns:mml="http://www.w3.org/1998/Math/MathML" id="M1"><mi>ϕ</mi></math><graphic specific-use="big" xmlns:xlink="http://www.w3.org/1999/xlink" xlink:href="alternativeImage/4FA0D3A8-3768-49be-9998-80DFC53A7C3B-M001.jpg"><?fx-imagestate width="3.64066648" height="5.07999992"?></graphic><graphic specific-use="small" xmlns:xlink="http://www.w3.org/1999/xlink" xlink:href="alternativeImage/4FA0D3A8-3768-49be-9998-80DFC53A7C3B-M001c.jpg"><?fx-imagestate width="3.64066648" height="5.07999992"?></graphic></alternatives></inline-formula>44.5 mm×10 mm小口径管多层多道焊温度场及热影响区特征数值模拟

姜海峰; 蔡文河; 刘海江; 张明申; 王庆峰; 周浩; 陈重毅

doi:10.20057/j.1003-8620.N260138

您当前的位置：

首页 >

文章列表页 >

G115钢

ϕ

44.5 mm×10 mm小口径管多层多道焊温度场及热影响区特征数值模拟

更新时间：2026-10-28

- G115钢 $ϕ$ 44.5 mm×10 mm小口径管多层多道焊温度场及热影响区特征数值模拟
- Numerical Simulation of Temperature Field and Heat-affected Zone Characteristics in Multi-layer and Multi-pass Welding of a $ϕ$ 44.5 mm × 10 mm Small-Diameter G115 Steel Pipe
- 特殊钢 2026年页码：1-7
- 作者机构：
  
  1.大唐郓城发电有限公司，郓城 274700
  2.中国大唐集团科学技术研究总院有限公司，北京 102200
  3.中国大唐集团科学技术研究总院有限公司华北电力试验研究院，北京 100040
  4.内蒙古科技大学材料科学与工程学院，包头 014010
- 作者简介：
  
  姜海峰（1986—），男，本科，正高级工程师； E-mail: jianghf0530@126.com
- 基金信息：
  
  国家重点研发计划(2024YFF0618905)
- DOI：10.20057/j.1003-8620.N260138
  中图分类号： TG40
- 收稿：2026-09-09，
  
  修回：2026-09-16，
  
  录用：2026-09-20，
  
  网络首发：2026-10-14，
- 稿件说明：
移动端阅览
姜海峰,蔡文河,刘海江等.G115钢ϕ44.5 mm×10 mm小口径管多层多道焊温度场及热影响区特征数值模拟[J].特殊钢,

Jiang Haifeng,Cai Wenhe,Liu Haijiang,et al.Numerical Simulation of Temperature Field and Heat-affected Zone Characteristics in Multi-layer and Multi-pass Welding of a ϕ44.5 mm × 10 mm Small-Diameter G115 Steel Pipe[J].Special Steel,
姜海峰,蔡文河,刘海江等.G115钢ϕ44.5 mm×10 mm小口径管多层多道焊温度场及热影响区特征数值模拟[J].特殊钢, DOI：.

Jiang Haifeng,Cai Wenhe,Liu Haijiang,et al.Numerical Simulation of Temperature Field and Heat-affected Zone Characteristics in Multi-layer and Multi-pass Welding of a ϕ44.5 mm × 10 mm Small-Diameter G115 Steel Pipe[J].Special Steel, DOI：.

G115钢

ϕ

44.5 mm×10 mm小口径管多层多道焊温度场及热影响区特征数值模拟

PDF下载

摘要

基于ANSYS有限元平台，建立G115钢小口径管（

https://html.publish.founderss.cn/rc-pub/api/common/picture?pictureId=120093096&type=

https://html.publish.founderss.cn/rc-pub/api/common/picture?pictureId=120093103&type=

2.03200006

2.87866688

44.5 mm×10 mm）多层多道焊三维热分析模型，采用双椭球热源和生死单元技术，模拟高、中、低三种焊接热输入（12、10、8 kJ·cm

-1

）下的瞬态温度场，研究热影响区（HAZ）热循环特征及宽度变化规律。结果表明：随热输入降低，第五层焊道熔合线附近峰值温度由1 741 ℃降至1 631 ℃，800 ℃到500 ℃冷却时间t

8/5

由24 s缩短至11 s，1 150 ℃以上停留时间由2.2 s减至1.1 s；HAZ总宽度由2.4 mm减小至1.5 mm，其中粗晶区由0.5 mm降至0.3 mm，细晶区由0.4 mm降至0.3 mm，临界相变区由0.7 mm降至0.5 mm。较小的焊接热输入可有效压缩FGHAZ和ICHAZ等薄弱区域，降低第Ⅳ型裂纹萌生风险；同时，道次增多、道次间冷却时间延长可减轻热积累。焊接热输入的选择应兼顾接头质量与焊接效率。

Abstract

Based on the ANSYS finite element platform， a three-dimensional thermal analysis model of multi-layer and multi-pass welding of a G115 steel small-diameter pipe （

https://html.publish.founderss.cn/rc-pub/api/common/picture?pictureId=120093096&type=

https://html.publish.founderss.cn/rc-pub/api/common/picture?pictureId=120093103&type=

2.03200006

2.87866688

44.5 mm × 10 mm） was established. The double ellipsoid heat source and element birth-death technique were adopted to simulate the transient temperature field under high， medium， and low welding heat inputs （12， 10， and 8 kJ/cm）， and the thermal cycle characteristics and the HAZ width variation were investigated. The results show that with decreasing heat input， the peak temperature near the fusion line of the fifth layer decreases from 1 741 ℃ to 1 631 ℃， the cooling time from 800 ℃ to 500 ℃ （t

8/5

） shortens from 24 s to 11 s， and the residence time above 1 150 ℃ reduces from 2.2 s to 1.1 s. The total HAZ width decreases from 2.4 mm to 1.5 mm， of which the coarse-grained HAZ decreases from 0.5 mm to 0.3 mm， the fine-grained HAZ from 0.4 mm to 0.3 mm， and the intercritical HAZ from 0.7 mm to 0.5 mm. A lower welding heat input can effectively compress the weak zones such as FGHAZ and ICHAZ， reducing the risk of Type IV cracking. Meanwhile， increasing the number of passes and prolonging inter-pass cooling time can alleviate heat accumulation. The selection of

welding heat input should balance joint quality and welding efficiency.

关键词

Keywords

references

刘正东，陈正宗，何西扣，等 . 630-700 ℃超超临界燃煤电站耐热管及其制造技术进展［J］. 金属学报， 2020 （ 4 ）： 539 - 548 .

何焕生，余黎明，刘晨曦，等 . 新一代马氏体耐热钢G115的研究进展［J］. 金属学报， 2022 ， 58 （ 3 ）： 311 - 323 .

张德金，危兆胜，王　萍，等 . G115钢焊接冷裂纹敏感性研究［J］. 金属加工（热加工）， 2022 （ 7 ）： 40 - 43+47

徐连勇，庞红宁，赵　雷，等 . G115钢CMT+P焊接工艺及组织和性能［J］. 焊接学报， 2020 ， 41 （ 8 ）： 1 - 5 +I0001.

马志宝，郭新芳，姜海峰，等 . G115钢TIPTIG焊接接头组织与性能研究［J］. 锅炉技术， 2024 ， 55 （ 6 ）： 51 - 55 .

李海昭，杜晋峰，梁军，等 . 焊接热输入对G115钢电弧焊接头组织和力学性能的影响［J］. 机械工程材料， 2025 ， 49 （ 12 ）： 27 - 32 .

陈重毅，李永清，陈正宗，等 . G115钢焊接热影响区组织特征［J］. 内蒙古科技大学学报， 2020 ， 39 （ 1 ）： 34 - 39 .

江骏东，马庆爽，陈乐利，等 . G115钢模拟热影响区界面组织演变研究［J］. 材料工程， 2024 ， 52 （ 11 ）： 91 - 106 .

张宇清，蒋涛，杨文佳，等 . G115钢窄间隙自动氩弧焊焊接接头的组织与性能研究［J］. 金属加工（热加工）， 2024 （ 10 ）： 29 - 33 .

莫春立，钱百年，国旭明，等 . 焊接热源计算模式的研究进展［J］. 焊接学报， 2001 ， 22 （ 3 ）： 93 - 96 .

蔡志鹏，赵海燕，鹿安理，等 . 焊接数值模拟中分段移动热源模型的建立及应用［J］. 中国机械工程， 2002 ， 13 （ 3 ）： 208 - 210 .

汪建华 . 焊接数值模拟技术及其应用［M］. 上海：上海交通大学出版社， 2003 .

Deng D A ， Murakawa H . Numerical simulation of temperature field and residual stress in multi-pass welds in stainless steel pipe and comparison with experimental measurements ［J］. Computational Materials Science ， 2006 ， 37 （ 3 ）： 269 - 277 .

Abe F ， Tabuchi M ， Kondo M ， et al . Suppression of Type IV fracture and improvement of creep strength of 9Cr steel welded joints by boron addition ［J］. International Journal of Pressure Vessels and Piping ， 2007 ， 84 （ 1-2 ）： 44 - 52 .

Francis J A ， Mazur W ， Bhadeshia H K D H . Review Type IV cracking in ferritic power plant steels ［J］. Materials Science and Technology ， 2006 ， 22 （ 12 ）： 1387 - 1395 .

浏览量

下载量

CSCD

文章被引用时，请邮件提醒。

提交

工具集

关联资源

CM690锚链钢淬火过程数值模拟及验证

基于ABAQUS的X70管线钢连铸板坯空冷的热力耦合分析

镍基单晶涡轮叶片定向凝固过程温度场数值模拟研究进展

水口浸入深度对结晶器内钢液流场与温度场的影响

双辐冷却低过热度浇铸结晶器流场和温度场耦合数值模拟

G115钢ϕ44.5 mm×10 mm小口径管多层多道焊温度场及热影响区特征数值模拟

Numerical Simulation of Temperature Field and Heat-affected Zone Characteristics in Multi-layer and Multi-pass Welding of a ϕ44.5 mm × 10 mm Small-Diameter G115 Steel Pipe

DOI：10.20057/j.1003-8620.N260138

摘要

Abstract

关键词

Keywords

references

G115钢 $ϕ$ 44.5 mm×10 mm小口径管多层多道焊温度场及热影响区特征数值模拟

Numerical Simulation of Temperature Field and Heat-affected Zone Characteristics in Multi-layer and Multi-pass Welding of a $ϕ$ 44.5 mm × 10 mm Small-Diameter G115 Steel Pipe